Lattics Parameters:

a=b=12.532Å, c=12.717Å, Z=6

Melting point

About 1095℃

Mohs Hardness

4

Density

3.85g/cm³

Thermal Conductivity

1.2W/m/K(_┴c): 1.6W/m/K(//c)

Thermal Expansion Coefficients

a11=4x10-6/K; a33=36x10-6/K

SHG Phase Matchable Range

409.6-3500nm(Type I)    525-3500nm(Type II)

therm-optic Coefficients(/℃)

dno/dT=-16.6X10-6 

dne/dT=-9.3X10-6 

Absorption Coefficients

<0.1%/cm at 1064nm         <1%/cm at 532nm

Angle Acceptance

0.8mrad-cm      (θ, Type I,1064 SHG)   
1.27mrad-cm    (θ, Type II,1064 SHG)

Temperature Acceptance

55℃-cm

Spectral Acceptance

1.1nm-cm

Walk-off Angle

2.7°   (Type I 1064 SHG)
3.2°  (Type II 1064 SHG)

NLO Coefficients

d_eff (I)=d₃₁sinθ+(d₁₁cosΦ-d₂₂sin3Φ)cosθ
d_eff (II)=(d₁₁sin3Φ+d₂₂cos3Φ)cos²θ

Non-vanished NLO susceptibilities

d₁₁=5.8xd₃₆(KDP)
d₃₁=0.05xd₁₁
d₂₂<0.05xd₁₁

sellmeier Equations(λ in μm )

n_o²=2.7359+0.01878 / (λ²-0.01822) -0.01354 λ²
n_e²=2.3753+0.01224 / (λ²-0.01667) -0.01516 λ²

Electro-optic coefficients:

r₂₂=2.7pm/V

Half-wave voltage:

7KV (at 1064nm,3*3*20mm3)

Resistivity:

>10¹¹ ohm-cm

Relative Dielectric Constant:

ε^s₁₁/ε_o:6.7
ε^s₃₃/ε_o:8.1
Tan δ<0.001